Effect of Al2O3 Seed-Layer on the Dielectric and Electrical Properties of Ultrathin MgO Films Fabricated Using in Situ Atomic Layer Deposition
Metal/insulator/metal (M/I/M) trilayers of Al/MgO/Al with ultrathin MgO in the thickness range of 2.20-4.40 nm were fabricated using in vacuo sputtering and atomic layer deposition (ALD). In order to achieve a high-quality metal/insulator (M/I) interface and hence high-quality dielectric ALD-MgO films, a 5 cycles (∼0.55 nm) thick ALD-Al2O3 seed layer (SL) was employed to demonstrate the dielectric constant (ϵr) is ∼8.82-9.38 in 3.30-4.95 nm thick ALD-MgO/SL films, which is close to that of single-crystal MgO ϵr ∼9.80. In contrast, a low ϵr of 3.55-4.66 for the ALD-MgO films of a similar thickness without a SL was observed. The effective oxide thickness (EOT) of ∼1.40 nm has therefore been achieved in the ultrathin ALD-MgO films, which are comparable to the EOTs of high-K dielectrics such as HfO2. In addition, the leakage current through the M/I/M structure is reduced by more than 1 order of magnitude with implementation of the SL. The high leakage current in the samples without a SL can be attributed to the nonuniform nucleation of the ALD-MgO on the Al surface with a significant portion of the Al surface remaining conductive as confirmed using in vacuo scanning tunneling spectroscopy (STS). With the SL, the STS study has confirmed a tunnel barrier height of 1.50 eV on 0.55 nm MgO with 0.55 nm Al2O3 SL with almost 100% coverage. In addition, molecular dynamics simulations point out the importance of deposition of ultrathin SL that has a significant effect on the initial nucleation of the Mg precursor. This result not only illustrates the critical importance of controlling the M/I interface to obtain high-quality dielectric properties of ultrathin ALD films but also provides an approach to engineering incompatible M/I interfaces using a SL for a high-quality dielectric required for applications in M/I/M tunnel junctions and complementary metal oxide semiconductors.
Physics, Astronomy, and Materials Science
capacitors, dielectric properties, in situ atomic layer deposition, in vacuo, metal/insulator interface, seed layer, ultrathin film
Acharya, Jagaran, Ryan Goul, Devon Romine, Ridwan Sakidja, and Judy Wu. "Effect of Al2O3 Seed-Layer on the Dielectric and Electrical Properties of Ultrathin MgO Films Fabricated Using In Situ Atomic Layer Deposition." ACS applied materials & interfaces 11, no. 33 (2019): 30368-30375.
ACS Applied Materials and Interfaces